Kobs India are manufacturers, stockiest & suppliers of Duplex Steel Buttweld End Cap. Duplex Steel Buttweld End Cap have special quality finishing and duress for long life, high pressure and zero defects. The product differentiation is based on the premier finish of Duplex Steel Buttweld End Cap with minimum burr at the edge .
The v shape formation for perfect welding and fabrication of the fittings in mega projects in oil and gas industry for long life of the product. Orders at Kobs India are guaranteed fast delivery of the Duplex Steel Buttweld End Cap in the country. The main reason being we have an excellent warehousing and storage facilities for both finished and semi finished goods.They are made ready as per the urgent requirements of the customers. The Duplex Steel Buttweld End Cap are manufactured to sustain very high pressure and product warranty.
Grade: 2205 (1.4507)
|Tensile strength||620MPa min||Density||7,805kg/m3|
|Yield strength||450MPa mi||Elastic modulus||200GPa|
Stainless Steel :
Grade: 304 (1.4301), 304L(1.4307), 304H (1.4948), 309 (1.4828), 309S, 310, 310S (1.4845), 316( 1.4401), 316H, 316L( 1.4404 /1.4432) , 317, 317L (1.4438), 321 (1.4541), 321 H(1.4878), 347 (1.4550), 347H (1.4961), 904L (1.4539)
Grade: Nickel 200, Nickel 201
Super Duplex Steel:
Grade: 2507 (UNS S32750), Z100
Grade: Inconel 600 (2.4640), Inconel 601 (2.4851), Inconel 625 (2.4856), Inconel 718(2.4668)
Grade: Gr.1 (3.7025) , Gr.2 (3.7035) , Gr.3(3.7055) , Gr.5(3.7164/65), Gr. 7(3.7235) , Gr. 11 (3.7225)
Grade: Monel 400 ( 2.4360) ( 2.4360), Monel K500 (2.4375), Monel R-405
Grade: Hastalloy B2, Hastalloy B3, Hastalloy C22, Hastalloy C276, Hastalloy X
Grade: Incoloy 800(2.4958), Incoloy 800H, Incoloy 800HT
The principal methods of hot working are extrusion, drawing, forging and rolling. Rolling is the most extensive employed forming process, though some limitations may apply to the process. Rolling mainly consists of three major sub-categories: flat rolling, shape rolling (with specifically designed roll grooves) and pipe rolling (including piercing). Forging may be sub-categorized as hamming, pressing, etc. .
Forging may be performed under hammers, in mechanical presses and upsetters or by a method known as roll forging. Pressing generally includes the manufacture of forged articles in hydraulic presses. Extrusion usually is performed in hydraulic presses which force the hot steel through a die. Rolling is performed in rolling mills of a variety of types. .
The two principal reasons for perform metal forming at elevated temperatures (hot working) are to reduce the forming loads through the reduction of the resistance of the steel to deformation, and to develop preferred metallurgical structures for strength and ductility of the finish products.
The most appropriate manufacturing method of a product will be decided with consideration of its material, sizes, shape, use, standards and other properties.